Self-Formulation Raw Materials
Composition: Resin、Plasticizers、Fillers、Flame Retardants、Polymer Additives、Silicon Masterbatch
Description: By taking advantage of our sourcing experience, and knowing the quality of raw materials, we are able to utilize our purchase power to find competitive raw materials with suitable quality. As key raw material for cable compounding, we are here to offer you a wide range of raw materials, mainly including the ones mentioned above.
Resin: PVC, CPE, CPVC, EPVC, EVA
| Resin | ||||||
| Brand | Grade | K value | Polymerization | Catagory | Characteristics | Package |
| S-PVC (Formosa Hanwha Haiwan Sinopec LG-Dagu/Hohai Huasu Shenfeng Wanhua Union/UPC) | K58 K60 K67 K70 K73 K85 K90 | 58 60 67 70 73 85 90 | 700 800 1000 1300 1400 2500 3000 | Ethylene based | See TDS | Small Bag Jumbo BagWith PalletWithout Pallet |
| CPE | 135A | Chlorine content 35% | Pipe, prodile, cable | |||
| CPVC | 500/700 | Chlorine content 63-72% | Extrusion type Injection type | |||
| EPVC | K65/ 70/ 72/ 75.5/ 76.5 | Wallpaper, leather, mats, floor, molding, toys, adhesive | ||||
| EVA | 7470M | VA content 26% | Injection, foaming, extrusion | |||
| 7235M | VA content 18% | |||||
| Plasticizers | |||||||
| Product | Appearance | Color (Pt-Co) | Content | Density | Flash Point | Acidity mgKOH/g | Package |
| DOTP | Transparent liquid | ≤50 | ≥99% | 0.92 | ≥210℃ | ≤0.1 | Drum IBC Flexitank |
| DOA | Transparent liquid | ≤50 | ≥99% | 0.924-0.930 | ≥190℃ | ≤0.1 | |
| TOTM | Transparent liquid | ≤40 | ≥99% | 0.987-0.997 | ≥250℃ | ≤0.15 | |
| ESO | Light yellow liquid | ≤150 | Epoxy ≥6.2% | 0.985-0.995 | ≥280℃ | ≤0.5 | |
| DOS | Transparent liquid | ≤30 | ≥99% | 0.913-0.919 | ≥210℃ | ≤0.15 | |
| Fillers | |||||
| Product | Content | Brightness | Impurity | Conductivity | Purpose |
| ATH (Aluminum hydroxide) | ≥99.5% | ≥97.5% | TDS | TDS | HFFR |
| Mg(OH)2 (Magnesium Hydroxide) | ≥99% | ≥97% | TDS | TDS | HFFR |
| TiO2-Anatase (Titanium Dioxide) | ≥98.5% | - | TDS | - | Pigment |
| TiO2-Rutile (Titanium Dioxide) | ≥97% | - | TDS | - | Pigment |
| Flame Retardants | |||||||
| Product | Appearance | Color (Pt-Co) | Phosphorus | Chlorine | Viscosity (mpa.s) | Moisture | Acidity (mgKOH/g) |
| TCPP | Little yellow liquid | ≤30 | 9.0-9.8% | 31.9-32.9% | 60-70 | ≤0.10% | ≤0.1 |
| TEP | Transparent liquid | ≤50 | ≥99% | 13.70% | - | - | ≤0.1 |
| Polymer Additives | ||
| Product | Brands | Application |
| Antioxidants MLAO Series | 1010, 1076, 168, 1024, 1520 etc. | PE, XLPE, Poe, HDPE, LDPE, PVE, EVA, PA, PUR, PP, POM, SBS, EPDM, PS, ABS etc. |
| Peroxide MLPO Series | DTBP,DCP,TCBP etc. | LDPE, HDPE, EVA, PVC, PP, PET, PS, PU, Acrylic, PC, PMMA, POM, PA, EVOH etc. |
| Processing Aid | PA based | Poe, EVA, PP, PE, POM, PET, PBT, ABS, HIPS, PA, POM, PUR, TPO, EPDM, TPE etc. |
| Stablizer | Ca/Zn based | |
| Impact Modifier | ACM, CPE based | |
| PVC Lubricant | Fatty ester, Stearic acid, OPE wax, Ca stearate | |
| Silicon Masterbatch | ||||
| Product | Appearance | Application | Dosage | Purpose |
| silicon masterbatch MLSM series | White Pellet | Wire and cable, Wires, Telecom pipes, Shoe sole, Engineer plastics, Color masterbatch, Elastomers, silane crosslinked-XLPE, PE, PP,PVC, PC, EVA | 0.2-5% | 1. Reduce friction, smoke and heat release rate. 2. Good stability, no migration. 3. Better compatibility, flowability, dispersion and hand feel. 4. Improve abrasion and scratch resistance. |